PRODUCT DESCRIPTION

Permatex High Temperature Anaerobic Flange Sealant is a

high temperature sealant specifically engineered for making

or dressing gaskets in rigid assemblies. It is able to withstand

temperatures up to 400℉(204℃)and fills gaps up to 0.020"

(primed)and permits clamping loads to be maintained for

strong, leakproof assemblies.

PRODUCT BENEFITS

● Seals all surface imperfections

● Seals most common automotive fluids

● No cracking or shrinking during cure

● Eliminates costly retorquing operations

● Single component system

● Non-corrosive to metal parts

TYPICAL APPLICATIONS

Seals close fitting joints between rigid metal faces and flanges.

Particularly suited where maximum temperature and chemical

resistance is required

DIRECTIONS FOR USE

1.Surfaces to be sealed should be free of grease, oil and

   dirt. Use Permatex Brake and Parts Cleaner to remove oil.

   Use Permatex Gasket Remover to remove old gaskets.

2.Apply manually to one side of flange, making sure a

   continuous bead is applied.

3.Reassemble parts, Flanges should be tightened as soon

   as possible after assembly to avoid shimming.

4.Torque to normal specifications.

5.Parts may be returned to service in one hour.

For Cleanup

1.Wipe off excess material with a clean cloth.

2.Clean hands with Permatex Fast Orange hand cleaner

  or soap and water.

For Disassembly

1.For smaller assembled parts, heat part to 400℉ to 4  50℉。

2.Use cautious, light prying or tapping motion to loosen the

   parts. Repeat heating/prying sequence as needed.

3.For larger assembled parts use prying/cleaving tools in

   combination with a light hammer and cautiously tap and

   pry the sides of the part to break the gasketed surfaces

   loose.

4.Once parts are disassembled, allow all surfaces to cool

  to room temperature.

5.Use Permatex Gasket Remover to remove dried anaerobic

   material

PHYSICAL PROPERTIES

                                                          Typical Value

Chemical Type                                Dimethacrylate Ester

Appearance                                             Gel

Color                                                       Red

Odor                                                     Acrid

Specific Gravity                                      1.08

Viscosity CP

     Brookfield HBT

     TC@2.5rpm                                        288,000

         @20rpm                                            50,000

Gap cure(inch)                              0.010 diametral(Unprimed)

                                                      0.020 diametral(Primed)

Cure Speed(Hours)                             1-12(Unprimed)

                                                       15 Minutes- 2(Primed)

Flash Point(℉)                                                 >200

TYPICAL CURING PERFORMANCE

Cure Speed vs.Substrate

The rate of cure will depend on the substrate used.The graph

below shows the shear strength developed with time on grit

blasted steel lap shears compared to different materials and

tested according to ASTM D 1002

Cure Speed VS.Activator

Where cure speed is unacceptably long,or large gaps are

present, applying activator to the surface will improve cure

speed. The graph below shows the shear strength developed

with time using Surface Prep Activator on grit blasted steel

lap shears and tested according to ASTM D1002

GENERAL INFORMATION

This product is not recommended for use in pure oxygen

and/ or oxygen rich system.

For safe handling information on this product, consult the

Material Safety Data Shet,(MSDS).

STORAGE

Products shall be ideally stored in a cool, dry location in

unopened containers at a temperature between 8 to 28 ℃

(46 to 82℉)unless otherwise labeled. Optimal storage is

at the lower half of this temperature range. To prevent

contamination of unused product, do not return any mate

rial to its original container.

NOTE

The data contained herein are furnished for information only

and are believed to be reliable. We can not assume respon

sibility for the results obtained by others over whose methods

we have no control. Permatex, Inc. specifically disclaims all

warranties expressed or implied, including warranties of mer

chantability or fitness for a particular purpose, arising from

sale or use of Permatex, Inc. products and disclaims any

liability for consequential or incidental damages of any kind,

including lost profits.This product may be covered by one

or more United States or foreign patents or patent applications.